Critical dimension control during template formation

ABSTRACT

Thickness of a residual layer may be altered to control critical dimension of features in a patterned layer provided by an imprint lithography process. The thickness of the residual layer may be directly proportional or inversely proportional to the critical dimension of features. Dispensing techniques and material selection may also provide control of the critical dimension of features in the patterned layer.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefit under 35 U.S.C. § 119(e)(1) of U.S. Provisional No. 61/031,759, filed on Feb. 27, 2008 and U.S. Provisional No. 61/108,914, filed on Oct. 28, 2008, both of which are hereby incorporated by reference herein.

BACKGROUND INFORMATION

Nano-fabrication includes the fabrication of very small structures that have features on the order of 100 nanometers or smaller. One application in which nano-fabrication has had a sizeable impact is in the processing of integrated circuits. The semiconductor processing industry continues to strive for larger production yields while increasing the circuits per unit area formed on a substrate, therefore nano-fabrication becomes increasingly important. Nano-fabrication provides greater process control while allowing continued reduction of the minimum feature dimensions of the structures formed. Other areas of development in which nano-fabrication has been employed include biotechnology, optical technology, mechanical systems, and the like.

An exemplary nano-fabrication technique in use today is commonly referred to as imprint lithography. Exemplary imprint lithography processes are described in detail in numerous publications, such as U.S. Patent Publication No. 2004/0065976, U.S. Patent Publication No. 2004/0065252, and U.S. Pat. No. 6,936,194, all of which are hereby incorporated by reference herein.

An imprint lithography technique disclosed in each of the aforementioned U.S. patent publications and patent includes formation of a relief pattern in a formable (polymerizable) layer and transferring a pattern corresponding to the relief pattern into an underlying substrate. The substrate may be coupled to a motion stage to obtain a desired positioning to facilitate the patterning process. The patterning process uses a template spaced apart from the substrate and a formable liquid applied between the template and the substrate. The formable liquid is solidified to form a rigid layer that has a pattern conforming to a shape of the surface of the template that contacts the formable liquid. After solidification, the template is separated from the rigid layer such that the template and the substrate are spaced apart. The substrate and the solidified layer are then subjected to additional processes to transfer a relief image into the substrate that corresponds to the pattern in the solidified layer.

BRIEF DESCRIPTION OF DRAWINGS

So that the present invention may be understood in more detail, a description of embodiments of the invention is provided with reference to the embodiments illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of the invention, and are therefore not to be considered limiting of the scope.

FIG. 1 illustrates a simplified side view of a lithographic system in accordance with an embodiment of the present invention.

FIG. 2 illustrates a simplified side view of the substrate shown in FIG. 1 having a patterned layer positioned thereon.

FIG. 3 illustrates a flow chart for supplying replications of a template.

FIGS. 4A and 4B illustrate an exemplary field on a substrate during formation of a sub-master template.

FIG. 5 illustrates a graphical representation of exemplary variations of average critical dimension across a substrate at a pre-etch stage and at a post post-etch stage.

FIGS. 6A and 6B illustrate a top down view and simplified side views of exemplary variations in critical dimension between on edges and the center of a substrate.

FIG. 7 illustrates a graphical representation of exemplary variations of average critical dimension in relation to residual layer thickness wherein average critical dimension is inversely proportional and directly proportional to residual layer thickness.

FIG. 8 illustrates a graphical representation of exemplary variation of critical dimension after a descum etching process.

FIG. 9 illustrates a graphical representation of exemplary variation of critical dimension after a polymerizing etching process.

FIG. 10 illustrates a flow chart of a method for controlling the magnitude of critical dimension of features using an etching process.

FIGS. 11A and 11B illustrate simplified side views of substrates having residual layers with different magnitudes of thickness.

FIG. 12 illustrates a flow chart of a method for controlling critical dimension of features using a dispensing technique.

DETAILED DESCRIPTION

Referring to the figures, and particularly to FIG. 1, illustrated therein is a lithographic system 10 used to form a relief pattern on substrate 12. Substrate 12 may be coupled to substrate chuck 14. As illustrated, substrate chuck 14 is a vacuum chuck. Substrate chuck 14, however, may be any chuck including, but not limited to, vacuum, pin-type, groove-type, electrostatic, electromagnetic, and/or the like. Exemplary chucks are described in U.S. Pat. No. 6,873,087, which is hereby incorporated by reference herein.

Substrate 12 and substrate chuck 14 may be further supported by stage 16. Stage 16 may provide motion along the x, y, and z axes. Stage 16, substrate 12, and substrate chuck 14 may also be positioned on a base (not shown).

Spaced-apart from substrate 12 is template 18. Template 18 may include mesa 20 extending therefrom towards substrate 12, mesa 20 having a patterning surface 22 thereon. Further, mesa 20 may be referred to as mold 20. Alternatively, template 18 may be formed without mesa 20.

Template 18 and/or mold 20 may be formed from such materials including, but not limited to, fused-silica, quartz, silicon, organic polymers, siloxane polymers, borosilicate glass, fluorocarbon polymers, metal, hardened sapphire, and/or the like. As illustrated, patterning surface 22 comprises features defined by a plurality of spaced-apart recesses 24 and/or protrusions 26, though embodiments of the present invention are not limited to such configurations. Patterning surface 22 may define any original pattern that forms the basis of a pattern to be formed on substrate 12.

Template 18 may be coupled to chuck 28. Chuck 28 may be configured as, but not limited to, vacuum, pin-type, groove-type, electrostatic, electromagnetic, and/or other similar chuck types. Exemplary chucks are further described in U.S. Pat. No. 6,873,087, which is hereby incorporated by reference herein. Further, chuck 28 may be coupled to imprint head 30 such that chuck 28 and/or imprint head 30 may be configured to facilitate movement of template 18.

System 10 may further comprise fluid dispense system 32. Fluid dispense system 32 may be used to deposit polymerizable material 34 on substrate 12. Polymerizable material 34 may be positioned upon substrate 12 using techniques such as drop dispense, spin-coating, dip coating, chemical vapor deposition (CVD), physical vapor deposition (PVD), thin film deposition, thick film deposition, and/or the like. For example, polymerizable material 34 may be positioned upon substrate 12 using techniques such as those described in U.S. Patent Publication No. 2005/0270312 and U.S. Patent Publication No. 2005/0106321, both of which are hereby incorporated by reference herein. Polymerizable material 34 may be disposed upon substrate 12 before and/or after a desired volume is defined between mold 20 and substrate 12 depending on design considerations. Polymerizable material 34 may comprise a monomer mixture as described in U.S. Pat. No. 7,157,036 and U.S. Patent Publication No. 2005/0187339, both of which are hereby incorporated by reference herein.

Referring to FIGS. 1 and 2, system 10 may further comprise energy source 38 coupled to direct energy 40 along path 42. Imprint head 30 and stage 16 may be configured to position template 18 and substrate 12 in superimposition with path 42. System 10 may be regulated by processor 54 in communication with stage 16, imprint head 30, fluid dispense system 32, and/or source 38, and may operate on a computer readable program stored in memory 56.

Either imprint head 30, stage 16, or both vary a distance between mold 20 and substrate 12 to define a desired volume therebetween that is filled by polymerizable material 34. For example, imprint head 30 may apply a force to template 18 such that mold 20 contacts polymerizable material 34. After the desired volume is filled with polymerizable material 34, source 38 produces energy 40, e.g., ultraviolet radiation, causing polymerizable material 34 to solidify and/or cross-link conforming to a shape of surface 44 of substrate 12 and patterning surface 22, defining patterned layer 46 on substrate 12. Patterned layer 46 may comprise a residual layer 48 and a plurality of features shown as protrusions 50 and recessions 52, with protrusions 50 having a thickness t₁ and residual layer having a thickness t₂.

The above-mentioned system and process may be further employed in imprint lithography processes and systems referred to in U.S. Pat. No. 6,932,934, U.S. Patent Publication No. 2004/0124566, U.S. Patent Publication No. 2004/0188381, and U.S. Patent Publication No. 2004/0211754, all of which are hereby incorporated by reference herein.

As template 18 may be expensive to manufacture, replications of a template 18 may aid in reducing manufacturing costs. FIG. 3 illustrates a flow diagram for supplying such replications. Generally, template 18, hereinafter referred to as master template 18, may be replicated to form a plurality of sub-master templates 60. These sub-master templates 60 may then form working templates 62 and/or patterned wafers for device fabrication. Additionally, master template 18 may form working templates 62 and/or patterned wafers for device fabrication. The device wafers may be patterned as a whole substrate or in a step and repeat manner described in further detail in S. V. Sreenivasan, “Nano-Scale Manufacturing Enabled by Imprint Lithography,” MRS Bulletin, Special Issue on Nanostructured Materials in Information Storage, Vol. 33, September 2008, pp. 854-863, which is hereby incorporated by reference herein. For simplicity in description, the systems and methods described herein below refer to formation of sub-master template 60. However, one skilled in the art will appreciate that the techniques described herein may be used in formation of working template 62, master template 18, patterned wafers and/or generally formation of a structure on substrate 12 using imprint lithography. It should be noted that although patterned wafers are illustrated in FIG. 3, the systems and methods described herein may be applied to other imprint lithography processes (e.g., whole wafer imprinting, CMOS imprinting, and the like).

Referring to FIGS. 4A and 4B, using the step and repeat process, sub-master template 60 may be formed by patterning multiple fields 80 a-801 across substrate 12. A portion of field 801 is illustrated in FIG. 4B. Features 50 a and/or 52 a formed on substrate 12 may have a critical dimension 70. For example, critical dimension 70 may be a width of feature 50 a.

During formation of sub-master template 60, patterned layer 46 a may have non-uniform critical dimension 70 across substrate 12 resulting from e-beam patterning, etching of master template 18, replicate etching, and/or the like. For example, as etching rates may vary at the edges of substrate 12 and/or transition points between materials, patterned layer 46 a may have non-uniform critical dimension 70 resulting from relative loading of materials (e.g., resist, chrome, and/or the like). In this situation, a uniform thickness t₁ of residual layer 48 a may exacerbate this non-uniformity.

Additionally, any non-uniformity of features 24 and/or 26 in master template 18 (shown in FIG. 3) may result in non-uniform critical dimensions 70 of features 50 a and/or 52 a during formation of sub-master template 62. FIG. 5 is a graphical representation of exemplary variations of average critical dimension 70 across substrate 12 a at a pre-etch stage and at a post post-etch stage. At the pre-etch stage, the average critical dimension 70 across a pattern may vary based on non-uniformity of master template 18 by which it may be formed. Additionally, at the post-etch stage, variation of the average critical dimension 70 may be further exacerbated.

Critical dimension 70 may also be varied across patterned layer 48 a due to processing and/or other similar conditions. For example, as illustrated in FIGS. 6A and 6B, critical dimension 70 at the inner edge 90 and the outer edge 92 of a pattern may be different than critical dimension 70 at the center 94 of the pattern.

As illustrated in FIGS. 4B and 7, the magnitude of critical dimension 70 of features 50 a and/or 52 a may be determined as a function of thickness t₃ of residual layer 48 a. As such, thickness t₃ of residual layer 48 a may be altered to control critical dimension 70 of features 50 a and/or 52 a. Thickness t₃ of residual layer 48 a may be directly proportional or inversely proportional to critical dimension 70 of features 50 a and/or 52 a. For example, thickness t₃ of residual layer 48 a may be altered to be directly proportional and as such provide substantially uniform critical dimension 70 across substrate 12, shown by Process A in FIG. 7. Alternatively, thickness t₃ of residual layer 48 a may be altered to be inversely proportional and as such provide variations in magnitude of critical dimension 70 across substrate 12, shown as Processes B and C in FIG. 7.

Etching Processes

Referring to FIGS. 4B, 8 and 9, an etching process may be used to alter thickness t₃ of residual layer 48 a to provide control of critical dimension 70 of features 50 a and/or 52 a. For example, a descum etching process (e.g., O₂/Ar composition) may be used to alter thickness t₃ of residual layer 48 a. FIG. 8 illustrates a graphical representation of exemplary variation of critical dimension 70 after a descum etching process. As shown, an approximate 3 nm variation in thickness t₃ may provide an approximate 1 nm variation of critical dimension 70 of features 50 a and/or 52 a. Alternatively, a polymerizing etch process (e.g., CF₄/CHF₃/Ar composition) may be used to alter thickness t₃ of residual layer 48 a. Additionally, the timing of the etch process may be used to control the variation in thickness t₃. For example, a longer etching time may be used to further reduce the critical dimension 70.

FIG. 9 illustrates a graphical representation of exemplary variation of critical dimension 70 after a polymerizing etch process. As shown, an approximate 1 nm variation among critical dimension 70 of features 50 a and/or 52 a may be expected from approximately 4.5 nm of thickness t₁.

FIG. 10 illustrates a flow chart of a method 100 for controlling the magnitude of critical dimension 70 of features 50 a and/or 52 a using an etching process. In a step 102, mold 20 and substrate 12 may be positioned to define a desired volume therebetween capable of being filled by polymerizable material 34. In a step 104, desired volume may be filled with polymerizable material 34. In a step 106, source 38 may produce energy 40, e.g., ultraviolet radiation, causing polymerizable material 34 to solidify and/or cross-link conforming to a shape of surface 44 of substrate 12 and patterning surface 22, defining patterned layer 46 on substrate 12. Patterned layer 46 may comprise residual layer 48 a and a plurality of features shown as protrusions 50 a and recessions 52 a, with residual layer having thickness t₃. In a step 108, thickness t₃ of residual layer 48 a may be determined and a desired critical dimension may be determined. In a step 110, a first etching composition may be applied to patterned layer 46 based on thickness t₃ of residual layer 48 a alter the critical dimension of features 70 to the desired critical dimension. The first etching composition may thus be provided to control magnitude of critical dimension 70 of features 50 a and/or 52 a. It should be noted that the desired critical dimension and the critical dimension 70 of features 50 a and/or 52 a may be similar. In a step 112, a second etching composition may be applied to patterned layer 46 to etch features 50 a and/or 52 a into substrate 12.

Dispense Techniques

Thickness t₃ of residual layer 48 a may also be altered by adjusting dispensing of polymerizable material 34 on substrate 12. For example, FIG. 11A illustrates substrate 12 a having residual layer 48 b with thickness t₄ and FIG. 11B illustrates substrate 12 b having residual layer 48 c with thickness t₅. The additional thickness t₄ of residual layer 48 b formed in FIG. 11A, as compared to FIG. 11B, may provide etching that is relatively more protective of the sidewall. This may result in less variation in critical dimension 70 than the thinner residual layer 48 c in FIG. 10B.

Referring to FIGS. 1 and 4B, dispensing techniques may be used to control critical dimension 70 of features 50 a and/or 52 a. For example, dispensing techniques may be used to provide residual layer 48 a with thickness t₃. Thickness t₃ of residual layer 48 a may be selected by the dispensing and positioning of polymerizable material 34 on substrate 12. The magnitude of critical dimension 70 of features 50 a and/or 52 a may be a function of the thickness t₃ of residual layer 48 a. As such, dispensing and positioning of polymerizable material 34 on substrate 12 may control critical dimension 70 of features 50 a and/or 52 a. Exemplary dispensing techniques may include, but are not limited to, techniques further described in U.S. Ser. No. 11/143,092, U.S. Ser. No. 10/868,683, U.S. Ser. No. 10/858,566, U.S. Ser. No. 10/714,088, U.S. Ser. No. 11/142,808, U.S. Ser. No. 10/191,749, and the like.

FIG. 12 illustrates a flow chart of a method 120 for controlling critical dimension 70 of features 50 a and/or 52 a using a dispensing technique. In a step 122, mold 20 and substrate 12 may be positioned to define a desired volume therebetween capable of being filled by polymerizable material 34. In a step 124, a dispense pattern of polymerizable material 34 for filling the desired volume may be determined. In a step 126, the dispense pattern may be adjusted to provide varying thickness t₂ of residual layer 48 a. For example, the dispense pattern may be adjusted for dispensing a greater amount of polymerizable material 34 at the edges of field 80. In a step 128, polymerizable material 34 may be dispensed based on the dispense pattern. In a step 130, source 38 may produce energy 40, e.g., ultraviolet radiation, causing polymerizable material 34 to solidify and/or cross-link conforming to a shape of surface 44 of substrate 12 and patterning surface 22, defining patterned layer 46 on substrate 12. Patterned layer 46 may comprise residual layer 48 a and a plurality of features shown as protrusions 50 a and recessions 52 a, with protrusions 50 a having thickness t₁ and residual layer having thickness t₃. In a step 132, thickness t₂ of residual layer 48 a may be determined. In a step 134, a first etching composition may be applied to patterned layer 46 based on thickness t₃ of residual layer 48 a to control magnitude of critical dimension 70 of features 50 a and/or 52 a. In a step 136, a second etching composition may be applied to patterned layer 46 to etch features 50 a and/or 52 a into substrate 12.

Erosion Rate

Differing polymerizable material 34 may have different erosion rates under the same etching process. As such, polymerizable material 34 with slower erosion rates may retain substantially uniform critical dimension 70 during an etching process than polymerizable material 34 having a faster erosion rate. By including different types of polymerizable material 34 having different erosion rates, critical dimension 70 of features 50 a and/or 52 a may be varied and/or controlled. For example, regions having a faster etch rate in an etch chamber may be imprinted using a slower-eroding polymerizable material 34. The slower-eroding polymerizable material 34 may minimize variations in critical dimension 70 of features 50 a and/or 52 a. In a similar fashion, regions that etch slower in an etch chamber may be imprinted using a faster-eroding polymerizable material 34. By varying the type of polymerizable material 34 dispensed on substrate 12, critical dimension 70 of features 50 a and/or 52 a may be controlled and/or be substantially uniform. 

1. A method comprising: positioning an imprint lithography mold in superimposition with a substrate to define a volume; dispensing polymerizable material within the volume; solidifying the polymerizable material to form a patterned layer having a residual layer and a plurality of features, the features having a critical dimension; determining a magnitude of thickness of the residual layer and a desired critical dimension for the features; applying a first etching composition to the patterned layer based on the magnitude of the thickness of the residual layer to alter the critical dimension of the features to the desired critical dimension; and, applying a second etching composition to the patterned layer to transfer the features into the substrate.
 2. The method of claim 1, wherein the first etching composition is a descum etching composition.
 3. The method of claim 1, wherein the first etching composition is a polymerizing etching composition.
 4. The method of claim 1, where in the first etching composition and the second etching composition are the same.
 5. The method of claim 1, further comprising: determining a dispense pattern for dispensing polymerizable material within the volume; and, adjusting the dispense pattern to vary the thickness of the resulting residual layer.
 6. The method of claim 5, wherein the thickness of the residual layer is greater at the edges of the substrate than at the center of the substrate.
 7. The method of claim 5, wherein the thickness of the residual layer is greater at the center of the substrate than at least one edge of the substrate.
 8. The method of claim 1, wherein applying a second etching composition to the patterned layer to transfer the features into the substrate forms a sub-master template.
 9. The method of claim 1, wherein the imprint mold is included in a sub-master template and applying a second etching composition to the patterned layer to transfer the features into the substrate forms a working template.
 10. The method of claim 1, wherein the imprint mold is included in a master template and applying a second etching composition to the patterned layer to transfer the features into the substrate form a working template.
 11. The method of claim 1, wherein the polymerizable material comprises a first polymerizable material and a second polymerizable material, the first polymerizable material having a first erosion rate that is greater than the second polymerizable material.
 12. The method of claim 1, wherein the residual layer thickness is proportional to the desired critical dimension.
 13. The method of claim 12, wherein the residual layer thickness is inversely proportional to the desired critical dimension.
 14. The method of claim 12, wherein the residual layer thickness is directly proportional to the desired critical dimension.
 15. A method comprising: positioning an imprint lithography mold and a substrate in superimposition to define a volume therebetween; dispensing a first polymerizable material on the substrate; dispensing a second polymerizable material on the substrate, the first polymerizable material having a first erosion rate that is greater than the second polymerizable material; solidifying the first polymerizable material and the second polymerizable material to form a patterned layer having a residual layer and a plurality of features, wherein a critical dimension of features is substantially uniform.
 16. The method of claim 15, further comprising: determining a dispense pattern for dispensing polymerizable material within the volume; and, adjusting the dispense pattern to vary the thickness of the resulting residual layer to be proportional to the critical dimension of features.
 17. A method comprising, positioning an imprint lithography mold in superimposition with a substrate to define a volume; dispensing polymerizable material within the volume; solidifying the polymerizable material to form a patterned layer having a residual layer and a plurality of features, the features having a critical dimension; determining a magnitude of thickness of the residual layer; and, applying a first etching composition to the patterned layer based on the magnitude of the thickness of the residual layer such that the residual layer thickness is proportional to the critical dimension.
 18. The method of claim 17, wherein the residual layer thickness is directly proportional to the critical dimension.
 19. The method of claim 17, wherein the residual layer thickness is indirectly proportional to the critical dimension.
 20. The method of claim 17, further comprising applying a second etching composition to the patterned layer to transfer the features into the substrate. 